| Property | Test Condition | Unit | Standard | Value |
| Rheological properties |
| | Mold shrinkage, flow/cross to flow | Value range based on general practical experience | in/in | ASTM D955 | 0.008 |
| Mechanical properties (23 °C/50 % r. h.) |
| | Flexural modulus | 158 °F | lb/in² | ASTM D790 | 5200 |
| | Flexural modulus | -22 °F | lb/in² | ASTM D790 | 323900 |
| | Tensile strength | | lb/in² | ASTM D412 | 6000 |
| | Ultimate elongation | | % | ASTM D412 | 450 |
| | Tensile stress at 50 % elongation | | lb/in² | ASTM D412 | 1400 |
| | Tensile stress at 100 % elongation | | lb/in² | ASTM D412 | 1600 |
| | Tensile stress at 300 % elongation | | lb/in² | ASTM D412 | 3500 |
| | Compression set, as molded | 22 h at 73 °F | % | ASTM D395-B | 20 |
| | Compression set, as molded | 22 h at 158 °F | % | ASTM D395-B | 75 |
| | Compression set, as molded | 22 h at 212 °F | % | ASTM D395-B | 90 |
| | Compression set, post-cured | 22 h at 73 °F; post-cured 16 h at 230 °F | % | ASTM D395-B | 15 |
| | Compression set, post-cured | 22 h at 158 °F; post-cured 16 h at 230 °F | % | ASTM D395-B | 35 |
| | Compression set, post-cured | 22 h at 212 °F; post-cured 16 h at 230 °F | % | ASTM D395-B | 100 |
| | Compressive load | | lb/in² | ASTM D575 | 4096 |
| | Compressive load | 2% deflection | lb/in² | ASTM D575 | 75 |
| | Compressive load | 5% deflection | lb/in² | ASTM D575 | 289 |
| | Compressive load | 10% deflection | lb/in² | ASTM D575 | 591 |
| | Compressive load | 15% deflection | lb/in² | ASTM D575 | 866 |
| | Compressive load | 20% deflection | lb/in² | ASTM D575 | 1142 |
| | Compressive load | 25% deflection | lb/in² | ASTM D575 | 1437 |
| | Tear strength, Die C | | lbf/in | ASTM D624 | 775 |
| Thermal properties |
| | Glass transition temperature | DMA=Dynamic Mechanical Analysis | °F | DMA | -4.0 |
| | Vicat softening temperature | Rate A; 1 kg; 50 °C/h | °F | ASTM D1525 | 239 |
| | Coefficient of linear thermal expansion, flow/cross-flow | | in/in/°F | ASTM D696 | 7.0 E-05 |
| Other properties (23 °C) |
| | Specific gravity | | - | ASTM D792 | 1.22 |
| | Shore hardness | | D Scale | ASTM D2240 | 52 |
| | Taber abrasion | H-18 wheel; 1,000-g; 1,000 cycles | mg Loss | ASTM D3489 | 70 |
| | Bayshore resilience | | % | ASTM D2632 | 25 |