[ Datasheet Texin 950 U]

Property		Test Condition	Unit	Standard	Value
Rheological properties
	Mold shrinkage, flow/cross to flow	Value range based on general practical experience	in/in	ASTM D955	0.008
Mechanical properties (23 °C/50 % r. h.)
	Flexural modulus	73 °F	lb/in²	ASTM D790	16500
	Flexural modulus	158 °F	lb/in²	ASTM D790	6800
	Tensile strength		lb/in²	ASTM D412	6000
	Ultimate elongation		%	ASTM D412	400
	Tensile stress at 50 % elongation		lb/in²	ASTM D412	1750
	Tensile stress at 100 % elongation		lb/in²	ASTM D412	2000
	Tensile stress at 300 % elongation		lb/in²	ASTM D412	4000
	Compression set, as molded	22 h at 73 °F	%	ASTM D395-B	20
	Compression set, as molded	22 h at 158 °F	%	ASTM D395-B	70
	Compression set, post-cured	22 h at 73 °F; post-cured 16 h at 230 °F	%	ASTM D395-B	15
	Compression set, post-cured	22 h at 158 °F; post-cured 16 h at 230 °F	%	ASTM D395-B	40
	Compressive load	2% deflection	lb/in²	ASTM D575	150
	Compressive load	5% deflection	lb/in²	ASTM D575	425
	Compressive load	10% deflection	lb/in²	ASTM D575	800
	Compressive load	15% deflection	lb/in²	ASTM D575	1100
	Compressive load	20% deflection	lb/in²	ASTM D575	1500
	Compressive load	25% deflection	lb/in²	ASTM D575	1800
	Compressive load	50% deflection	lb/in²	ASTM D575	4500
	Tear strength, Die C		lbf/in	ASTM D624	750
Thermal properties
	Glass transition temperature	DMA=Dynamic Mechanical Analysis	°F	DMA	-17
	Low-temperature brittle point		°F	ASTM D746	< -90
	Vicat softening temperature	Rate A; 5 kg; 50 °C/h	°F	ASTM D1525	262
Other properties (23 °C)
	Specific gravity		-	ASTM D792	1.15
	Shore hardness		D Scale	ASTM D2240	50
	Taber abrasion	H-18 wheel; 1,000-g; 1,000 cycles	mg Loss	ASTM D3489	75
	Bayshore resilience		%	ASTM D2632	35

Disclaimer

Aromatic polyether-based thermoplastic polyurethane with a Shore D hardness of approximately 50. UV stabilized. Can be injection molded or extruded., Applications include gasketed hose, tubing, shoe inserts, connectors, and belting.